Titre : Low-cycle fatigue crack initiation and break in strain-life curve of Al-Li 8090 alloy.

Cité dans : [DATA062] Recherche sur les auteurs COFFIN et MANSON, octobre 2001.

Source : Metallurgical and Materials Transactions A: Physical Metallurgy and Materials Science v 30A n 3 Mid Mar 1999.p 887-890
CODEN : MMTAEB
ISSN : 1073-5623
Année : 1999
Document_Type : Journal
Treatment_Code : Experimental
Language : English
Stockage :

Abstract :
The low-cycle fatigue tests were conducted at an ambient temperature
for both the peak-aged and solutionized samples of Al-Li 8090
alloy.The peak-aged alloy exhibited two characteristic strain
amplitude ranges having different slopes in the cyclic
stress-plastic strain curve, while the solutionized alloy showed
only a single slope in the curve, indicating that the operative
deformation mode for the peak-aged alloy is different at two strain
amplitude ranges.The peak-aged alloy revealed the break in the
Coffin-Manson curve at the same plastic strain amplitude as in the
cyclic stress-strain curve.On the other hand, the solutionized alloy
did not show any break in the Coffin-Manson curve.

References : 9 Refs.

Accession_Number : 1999(21):1013

Mise à jour le lundi 10 avril 2023 à 18 h 59 - E-mail : thierry.lequeu@gmail.com
Cette page a été produite par le programme TXT2HTM.EXE, version 10.7.3 du 27 décembre 2018.

Copyright 2023 :

Les informations contenues dans cette page sont à usage strict de Thierry LEQUEU et ne doivent être utilisées ou copiées par un tiers.
Powered by www.google.fr, www.e-kart.fr, l'atelier d'Aurélie - Coiffure mixte et barbier, La Boutique Kit Elec Shop and www.lequeu.fr.